Structural and Electronic Properties of Indium-Doped n-type Cd-Se-Te Crystals

We present a comprehensive investigation into the potential of n-type indium-doped cadmium selenide telluride (CST:In) as a high-performance candidate for solar cell applications, without the need for resource-intensive post-growth treatments that are required for CdTe:In. We compared undoped CST and CST:In crystals under different growth conditions, analyzing their structural and electronic properties using x-ray diffraction (XRD), electron probe microanalysis (EPMA), current–voltage (IV) and Hall effect measurements, time-resolved photoluminescence (TRPL), optical transmission, and photoluminescence (PL) mapping. The results reveal that as-grown CST:In crystals achieve nearly 100% carrier activation, yielding an electron concentration of 9.5 × 10¹⁸ cm⁻³, mobility of 653 cm²/V·s and a 5 ns lifetime which approaches the radiative limit. Furthermore, comparison of PL maps from crystal growths having different cooling profiles suggests a strong effect of cooling rate on selenium segregation and cubic/hexagonal/polytype phase distribution. Slower cooling leads to a more homogeneous cubic structure with lower Se segregation, while a faster cooling rate results in increased Se segregation, and twin boundaries and stacking faults with polytypic and hexagonal character.