<p>In this study, we explored the effect of Zn content on the static recrystallization of three 80 pct hot-compressed alloys, Mg–0.5Zn–0.1Ca wt pct (ZX050), Mg–1Zn–0.1Ca wt pct (ZX10), and Mg–3.2Zn–0.1Ca wt pct (ZX30), using far-field high-energy microscopy (ff-HEDM). Individual recrystallized grains were tracked and their 3D centroid, relative volume, and grain-averaged crystallographic orientation were measured during annealing. These measurements were used to compare the recrystallization kinetics and texture evolution of recrystallized grains in ZX alloys as a function of the Zn content. Fully recrystallized microstructures were observed for the ZX30 and the ZX10 alloys after annealing at 230&#xa0;°C and 330&#xa0;°C, respectively. In contrast, only a partially recrystallized microstructure for the ZX050 alloy was observed after &gt; 1 hour of annealing at 430&#xa0;°C. The resistance to recrystallization with decreasing Zn content was also confirmed by detecting faster growth rates of recrystallized grains in the ZX10 and ZX30 alloys, and slower growth rates in the ZX050 alloy. The significant recrystallization texture weakening of the ZX10 and ZX30 alloys and the development of a basal texture in the ZX05 alloy were described based on the orientation dependency of nucleation and growth of recrystallized grains. The analysis demonstrated that texture weakening was associated with increasing Zn content in Mg–Zn–Ca alloys.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Characterization of Recrystallized Grains During Static Recrystallization of Hot-Compressed Mg–Zn–Ca Alloys Using In Situ Far-Field High-Energy Diffraction Microscopy

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月2日

查看全文
  • Reza Roumina,
  • Sangwon Lee,
  • Tracy D. Berman,
  • Katherine S. Shanks,
  • John E. Allison,
  • Ashley Bucsek

摘要

In this study, we explored the effect of Zn content on the static recrystallization of three 80 pct hot-compressed alloys, Mg–0.5Zn–0.1Ca wt pct (ZX050), Mg–1Zn–0.1Ca wt pct (ZX10), and Mg–3.2Zn–0.1Ca wt pct (ZX30), using far-field high-energy microscopy (ff-HEDM). Individual recrystallized grains were tracked and their 3D centroid, relative volume, and grain-averaged crystallographic orientation were measured during annealing. These measurements were used to compare the recrystallization kinetics and texture evolution of recrystallized grains in ZX alloys as a function of the Zn content. Fully recrystallized microstructures were observed for the ZX30 and the ZX10 alloys after annealing at 230 °C and 330 °C, respectively. In contrast, only a partially recrystallized microstructure for the ZX050 alloy was observed after > 1 hour of annealing at 430 °C. The resistance to recrystallization with decreasing Zn content was also confirmed by detecting faster growth rates of recrystallized grains in the ZX10 and ZX30 alloys, and slower growth rates in the ZX050 alloy. The significant recrystallization texture weakening of the ZX10 and ZX30 alloys and the development of a basal texture in the ZX05 alloy were described based on the orientation dependency of nucleation and growth of recrystallized grains. The analysis demonstrated that texture weakening was associated with increasing Zn content in Mg–Zn–Ca alloys.