<p>A series of CoS<sub>2−<i>x</i></sub>Se<sub><i>x</i></sub> (<i>x</i>=0.05, 0.1, 0.2, 0.3, and 2) composite catalysts were synthesized on carbon fiber paper via the hydrothermal method with Se doping. By precisely controlling the reaction temperature and Se doping level, a hollow spherical catalyst structure composed of CoSSe was successfully synthesized, which exhibited exceptional activity for hydrogen evolution in acidic solutions. The influences of Se doping on the microstructure and catalytic mechanism of hydrogen evolution reaction (HER) of these composites were systematically investigated. The experimental results reveal that the hollow spherical sample displays an overpotential value of 143 mV along with a Tafel slope value of 69.8 mV·dec<sup>−1</sup> at a current density of 10 mA·cm<sup>−2</sup> in an acid aqueous solution. Furthermore, it demonstrates remarkable cycling stability after undergoing 3000 cycles. The comprehensive analysis indicates that Se doping optimizes the electronic structure and enhances conductivity, meanwhile the unique hollow spherical architecture increases active sites for HER and significantly improves overall electrocatalytic performance.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Hollow Spherical Structure CoS2−xSex for Electrocatalytic Hydrogen Evolution Reaction

  • 期刊论文

  • 发表日期：

    2025年7月24日

查看全文
  • Dandan Liang,
  • Ying Zhang,
  • Weili Hou,
  • Jihua Shang,
  • Haibo Ren,
  • Yufeng Sun

摘要

A series of CoS2−xSex (x=0.05, 0.1, 0.2, 0.3, and 2) composite catalysts were synthesized on carbon fiber paper via the hydrothermal method with Se doping. By precisely controlling the reaction temperature and Se doping level, a hollow spherical catalyst structure composed of CoSSe was successfully synthesized, which exhibited exceptional activity for hydrogen evolution in acidic solutions. The influences of Se doping on the microstructure and catalytic mechanism of hydrogen evolution reaction (HER) of these composites were systematically investigated. The experimental results reveal that the hollow spherical sample displays an overpotential value of 143 mV along with a Tafel slope value of 69.8 mV·dec−1 at a current density of 10 mA·cm−2 in an acid aqueous solution. Furthermore, it demonstrates remarkable cycling stability after undergoing 3000 cycles. The comprehensive analysis indicates that Se doping optimizes the electronic structure and enhances conductivity, meanwhile the unique hollow spherical architecture increases active sites for HER and significantly improves overall electrocatalytic performance.