<p>Impedance spectroscopy was used to study proton conductivity changing of pre-dried sulfonated perfluorinated and hydrocarbon (polynaphtoleimide) membranes over time during their hydration. For this purpose, commercial perfluorinated membranes Nafion 212, Nafion 211, Gore 18 and hydrocarbon co-polynaphthoyleneimide (co-PNIS) membranes with different hydrophobicity blocks (ODAS/MDAC and ODAS/MDOT) synthesized in this work were used. It was found that the proton conductivity steady state values of Gore 18 membrane were established faster in humidity atmosphere after its drying than for other membranes studied in this work. This membrane demonstrates also better characteristics with cyclic humidity changes from 35 to 75% (sorption) and from 75 to 35% (desorption), which actually simulates start operation of PEMFC after its storage at the normal conditions. It was found that Nafion type membranes possess more universal hydration characteristics PEMFC in whole investigated humidity values interval and reveal consistently both high proton transport values and proton conductivity recovery kinetics parameters from dry state. However, the proton conductivity highest level at RH &gt; 75% is demonstrated by fluorine-free co-PNIS membranes, which is also associated with its higher hydration degree compared to perfluorinated analogues. Moreover, it has been observed that the hydrocarbon co-PNIS (ODAS/MDOT) membrane, with a large difference in the hydrophobicity degree between polymer blocks is characterized by both higher protonic conductivity and its recovery kinetics parameters compared to the hydrocarbon analogue co-PNIS (ODAS/MDAC). The effect of the hydrophobic block on proton transport in co-PNIS membrane is discussed.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Comparative studies of the proton conductivity behavior during hydration of sulfonated perfluorinated and hydrocarbon proton exchange membranes

  • 期刊论文

  • 发表日期：

    2025年1月9日

查看全文
  • Ulyana M. Zavorotnaya,
  • Yaroslav E. Gudkov,
  • Igor I. Ponomarev,
  • Nikolay V. Lyskov,
  • Ivan A. Ryzhkin,
  • Vitaly V. Sinitsyn

摘要

Impedance spectroscopy was used to study proton conductivity changing of pre-dried sulfonated perfluorinated and hydrocarbon (polynaphtoleimide) membranes over time during their hydration. For this purpose, commercial perfluorinated membranes Nafion 212, Nafion 211, Gore 18 and hydrocarbon co-polynaphthoyleneimide (co-PNIS) membranes with different hydrophobicity blocks (ODAS/MDAC and ODAS/MDOT) synthesized in this work were used. It was found that the proton conductivity steady state values of Gore 18 membrane were established faster in humidity atmosphere after its drying than for other membranes studied in this work. This membrane demonstrates also better characteristics with cyclic humidity changes from 35 to 75% (sorption) and from 75 to 35% (desorption), which actually simulates start operation of PEMFC after its storage at the normal conditions. It was found that Nafion type membranes possess more universal hydration characteristics PEMFC in whole investigated humidity values interval and reveal consistently both high proton transport values and proton conductivity recovery kinetics parameters from dry state. However, the proton conductivity highest level at RH > 75% is demonstrated by fluorine-free co-PNIS membranes, which is also associated with its higher hydration degree compared to perfluorinated analogues. Moreover, it has been observed that the hydrocarbon co-PNIS (ODAS/MDOT) membrane, with a large difference in the hydrophobicity degree between polymer blocks is characterized by both higher protonic conductivity and its recovery kinetics parameters compared to the hydrocarbon analogue co-PNIS (ODAS/MDAC). The effect of the hydrophobic block on proton transport in co-PNIS membrane is discussed.