<p>In the transportation, maritime and aviation industries, aluminum alloys — particularly those in the 2xxx series (Al–Cu type) — are frequently used because they offer an ideal combination of properties, including toughness, a high strength-to-weight ratio and fatigue resistance. Graphene, a two-dimensional material with a single-atom thickness composed of carbon atoms arranged in a hexagonal lattice, attracts interest due to its remarkable properties and is commonly utilized as a reinforcement in composite materials. Few-layered graphene (FLG) reinforced Al–4 wt.% Cu matrix composites were prepared via mechanical alloying (MA, 500 rpm, ball-to-powder ratio 7 : 1), uniaxial pressing (300 MPa), and conventional sintering (59°C, 3 hours, argon gas flow). The present work investigates corrosion behaviors of FLG (0.25 and 0.5 wt.%) reinforced Al–4 wt.% Cu composites with different MA durations. Open-circuit potential (OCP), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) measurements were carried out in a 3.5% NaCl solution to determine the corrosion behavior. Following the corrosion test, X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) analysis were performed on the specimen that exhibited the optimum results. The data obtained before and after the test were compared to investigate the structural changes that occurred as a result of the corrosion test. The analysis demonstrated that the sample reinforced with 0.5 wt.% FLG and subjected to 7 hours of MA had the highest corrosion resistance.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effect of Few-Layered Graphene on the Corrosion Behaviour of the Al–Cu Matrix Composites

  • 期刊论文

  • 发表日期：

    2025年5月1日

查看全文
  • Cantekin Kaykilarli,
  • Taha Yasin Eken,
  • Burak Küçükelyas,
  • Deniz Uzunsoy

摘要

In the transportation, maritime and aviation industries, aluminum alloys — particularly those in the 2xxx series (Al–Cu type) — are frequently used because they offer an ideal combination of properties, including toughness, a high strength-to-weight ratio and fatigue resistance. Graphene, a two-dimensional material with a single-atom thickness composed of carbon atoms arranged in a hexagonal lattice, attracts interest due to its remarkable properties and is commonly utilized as a reinforcement in composite materials. Few-layered graphene (FLG) reinforced Al–4 wt.% Cu matrix composites were prepared via mechanical alloying (MA, 500 rpm, ball-to-powder ratio 7 : 1), uniaxial pressing (300 MPa), and conventional sintering (59°C, 3 hours, argon gas flow). The present work investigates corrosion behaviors of FLG (0.25 and 0.5 wt.%) reinforced Al–4 wt.% Cu composites with different MA durations. Open-circuit potential (OCP), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) measurements were carried out in a 3.5% NaCl solution to determine the corrosion behavior. Following the corrosion test, X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) analysis were performed on the specimen that exhibited the optimum results. The data obtained before and after the test were compared to investigate the structural changes that occurred as a result of the corrosion test. The analysis demonstrated that the sample reinforced with 0.5 wt.% FLG and subjected to 7 hours of MA had the highest corrosion resistance.