<p>The nitridation of three austenitic high-temperature alloys in 95% N<sub>2</sub> + 5% H<sub>2</sub> environment at 1100 °C was evaluated in terms of gravimetry and investigated by SEM–EDS, EPMA and STEM. Samples made from Alloy 600, 253 MA and 353 MA were exposed for 1 day, 1 week and 3 weeks. Alloy 600 underwent very little nitridation, while 253 MA and especially 353 MA, were heavily affected by nitride precipitation. The nitridation of all three alloys had reached equilibrium after three weeks; the extent of nitridation depending on the chromium activity in the alloy. The kinetics of nitrogen ingress into the alloy depends on nickel concentration, while the rate-determining step in the nitridation process is the nucleation and growth of the nitride precipitates.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Nitridation of Three Austenitic Alloys at 1100 °C

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年3月19日

查看全文
  • T. Sand,
  • A. Rajagopal,
  • M. Sattari,
  • S. Bigdeli,
  • M. Hättestrand,
  • J.-E. Svensson,
  • M. Halvarsson,
  • L.-G. Johansson

摘要

The nitridation of three austenitic high-temperature alloys in 95% N2 + 5% H2 environment at 1100 °C was evaluated in terms of gravimetry and investigated by SEM–EDS, EPMA and STEM. Samples made from Alloy 600, 253 MA and 353 MA were exposed for 1 day, 1 week and 3 weeks. Alloy 600 underwent very little nitridation, while 253 MA and especially 353 MA, were heavily affected by nitride precipitation. The nitridation of all three alloys had reached equilibrium after three weeks; the extent of nitridation depending on the chromium activity in the alloy. The kinetics of nitrogen ingress into the alloy depends on nickel concentration, while the rate-determining step in the nitridation process is the nucleation and growth of the nitride precipitates.