<p>The effect of microadditions of transition metals Zr, Hf, Ti, V on the kinetics of solid solution decomposition, recrystallization and strengthening characteristics of an ingot with diameter 92 mm, extruded strip, and cold-rolled sheets from alloy Al – 0.17 wt.% Sc is studied. It is shown that microalloying with zirconium is the most effective. The best combination of mechanical properties is obtained in the alloy when the content of zirconium is equal to that scandium, i.e. it is necessary to observe a 1-to-1 proportion of Sc to Zr. The addition of zirconium, which dissolves in the solid solution together with scandium, inhibits the decomposition of the solid solution in the ingots and increases the recrystallization temperature and significantly raises the strength in the deformed semiproducts.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effect of Microalloying with Transition Metals on the Structure and Properties of Alloy Al – 0.17Sc

  • 期刊论文

  • 发表日期：

    2025年3月1日

查看全文
  • V. V. Zakharov,
  • I. A. Fisenko

摘要

The effect of microadditions of transition metals Zr, Hf, Ti, V on the kinetics of solid solution decomposition, recrystallization and strengthening characteristics of an ingot with diameter 92 mm, extruded strip, and cold-rolled sheets from alloy Al – 0.17 wt.% Sc is studied. It is shown that microalloying with zirconium is the most effective. The best combination of mechanical properties is obtained in the alloy when the content of zirconium is equal to that scandium, i.e. it is necessary to observe a 1-to-1 proportion of Sc to Zr. The addition of zirconium, which dissolves in the solid solution together with scandium, inhibits the decomposition of the solid solution in the ingots and increases the recrystallization temperature and significantly raises the strength in the deformed semiproducts.