<p>The effect of isothermal annealing on the microstructure and mechanical properties of hypereutectoid steel U10A(W110, AISI/ASTM) for subsequent cold plastic deformation by rolling is studied. To increase the ductility of the steel, an isothermal annealing mode is suggested, which ensures satisfactory deformability during cold rolling. After such annealing and subsequent rolling with a relative reduction of 67%, the steel has the tensile strength values no lower than 1270 MPa as required for high-strength cold-rolled strips according to GOST 21996–76 and a hardness no lower than 375 <i>HV</i> without the risk of damage to the rolling rolls.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effect of Isothermal Annealing Before Cold Rolling on the Mechanical Properties of Hypereutectoid Steel for High-Strength Cold-Rolled Strips

  • 期刊论文

  • 发表日期：

    2025年1月1日

查看全文
  • I. D. Pospelov,
  • D. V. Matveeva

摘要

The effect of isothermal annealing on the microstructure and mechanical properties of hypereutectoid steel U10A(W110, AISI/ASTM) for subsequent cold plastic deformation by rolling is studied. To increase the ductility of the steel, an isothermal annealing mode is suggested, which ensures satisfactory deformability during cold rolling. After such annealing and subsequent rolling with a relative reduction of 67%, the steel has the tensile strength values no lower than 1270 MPa as required for high-strength cold-rolled strips according to GOST 21996–76 and a hardness no lower than 375 HV without the risk of damage to the rolling rolls.