<p>In this paper, a string of waterborne polyurethane (WPU) emulsions synergistically modified with PDMS and GMS were successfully prepared by incorporating Polydimethylsiloxane (PDMS) into the soft segments of waterborne polyurethanes, and using glycerol monostearate (GMS) as a chain extender. FTIR, TGA, SEM, particle size test, water contact angle and other tests were used to characterize the effects of variable GMS contents on the structure and function of WPUs. The experimental tests showed that the WPUs synthesised with 30% PDMS-8% GMS synergism had better overall performance. The water contact angle could reach 115.4°, and the water absorption was reduced to 10.52% at 72&#xa0;h. Furthermore, this innovative WPU film had excellent thermal stabilization, and this study provided a new approach to improve waterproofing performance, hydrophobicity and thermal stability of waterborne polyurethanes, which is expected to be applied in coatings, adhesives and water-resistant agents.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Novel waterborne polyurethanes extended by glycerol monostearate: their synthesis and application to water repellency

  • 期刊论文

  • 发表日期：

    2025年1月14日

查看全文
  • Haitao Zhou,
  • Yan Liu,
  • Tianhao Lu,
  • Wulin Xia,
  • Ying Qin,
  • Guankun Kuang,
  • Binjie Xin

摘要

In this paper, a string of waterborne polyurethane (WPU) emulsions synergistically modified with PDMS and GMS were successfully prepared by incorporating Polydimethylsiloxane (PDMS) into the soft segments of waterborne polyurethanes, and using glycerol monostearate (GMS) as a chain extender. FTIR, TGA, SEM, particle size test, water contact angle and other tests were used to characterize the effects of variable GMS contents on the structure and function of WPUs. The experimental tests showed that the WPUs synthesised with 30% PDMS-8% GMS synergism had better overall performance. The water contact angle could reach 115.4°, and the water absorption was reduced to 10.52% at 72 h. Furthermore, this innovative WPU film had excellent thermal stabilization, and this study provided a new approach to improve waterproofing performance, hydrophobicity and thermal stability of waterborne polyurethanes, which is expected to be applied in coatings, adhesives and water-resistant agents.