Material extrusion additive manufacturing of TPU blended ABS with particular reference to mechanical and damping performance

Thermoplastic polyurethane (TPU) has emerged as extremely benign materials for next-generation manufacturing using additive manufacturing processes due to its favorable mechanical properties, durability, and as well as biocompatibility. However, the lack of stiffness of TPU affects its buckling strength and performance efficiency. Therefore, an efficient method of optimization of a 3D-printable composition of TPU-based blends is necessary. In this work, attempts were made to explore material extrusion additive manufacturing technique of acrylonitrile–butadiene–styrene (ABS)/TPU blends with particular reference to mechanical and damping behaviour. Design of experiment (DoE) was used to determine the optimum printing parameters. Rheological studies were exploited to understand the printability, and optimum 3D-printable blend composition. The damping behaviour of each blend composition was calculated and a damping ratio (ξ) between \(1\le \xi \le 2\) $1\le \xi \le 2$ was observed for 40 wt% ABS loading, which raised to \(1\le \xi \le 4\) $1\le \xi \le 4$ for 80 wt% ABS loaded blend specimen. Furthermore, for ABS incorporated TPU, a significant enhancement of stiffness over neat TPU was achieved, thereby reasonably addressing the filament stiffness issue. This work introduces an efficient method of improving TPU filament printability while parallelly identifying the printable blend composition which can be beneficial for several potential applications.