<p>In the process of 25% K and 12.5% P-doped BaFe<sub>2</sub>As<sub>2</sub>, the decrease of Fe ions height is accompanied by the suppression of antiferromagnetic order. Both K and P-doping cause an increase in the distance between Fe–As layers and a contraction of Fe–As bonds, and the contraction of Fe–As bond seems to be one of the most sensitive factors affecting antiferromagnetic suppression. It is found that the contraction of Fe–As bonds tends to be coordinated with an increase in Fe–Fe average distance to ultimately suppress antiferromagnetism to a smaller value. Similar structural changes result in K/P-doping causing Lifshitz transition (LT) and electronic topological transition (ETT). At the Fermi level, K-doping increases the density of states of Fe 3<i>d</i> and As 4<i>p</i>, while P-doping reduces these values.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

First-Principles Study on the Structure and Electronic Structure of K and P-Doped Iron-Based Superconductor BaFe2As2

  • 期刊论文

  • 发表日期：

    2025年7月25日

查看全文
  • Li Li,
  • Zhihua Zhang,
  • Ming He,
  • Long Lin,
  • Yan Cui,
  • Hualong Tao,
  • Weifang Wang,
  • Hongli Wang,
  • Dongfang Jia,
  • Ying Gao,
  • Juan Li,
  • Sheng Zhan,
  • Peihan Yu,
  • Yufen Feng,
  • Huijie Ren,
  • Shuyue Qin,
  • Rubing Zhang,
  • Yuxuan Song,
  • Jingyi Shi

摘要

In the process of 25% K and 12.5% P-doped BaFe2As2, the decrease of Fe ions height is accompanied by the suppression of antiferromagnetic order. Both K and P-doping cause an increase in the distance between Fe–As layers and a contraction of Fe–As bonds, and the contraction of Fe–As bond seems to be one of the most sensitive factors affecting antiferromagnetic suppression. It is found that the contraction of Fe–As bonds tends to be coordinated with an increase in Fe–Fe average distance to ultimately suppress antiferromagnetism to a smaller value. Similar structural changes result in K/P-doping causing Lifshitz transition (LT) and electronic topological transition (ETT). At the Fermi level, K-doping increases the density of states of Fe 3d and As 4p, while P-doping reduces these values.