<p>With the development of pulsed power devices in the direction of miniaturization, integration, and safety, the development of dielectric capacitors with large energy storage density (<i>W</i><sub>rec</sub>), high energy storage efficiency (<i>η</i>), and decent energy storage stability has become an important topic that needs to be discussed in depth in the academic community. In this study, (1&#xa0;−&#xa0;<i>x</i>)(Bi<sub>0.5</sub>Na<sub>0.5</sub>)<sub>0.7</sub>Sr<sub>0.3</sub>TiO<sub>3</sub>-<i>x</i>La(Mg<sub>0.5</sub>Zr<sub>0.5</sub>)O<sub>3</sub> [(1&#xa0;−&#xa0;<i>x</i>)BNST-<i>x</i>LMZ] ceramics were prepared by traditional solid-phase method. Through rational component manipulation, the introduction of LMZ effectively disrupted the long-range ordered arrangement of the original matrix, constructing short-range polar nano-microregions that consequently delayed the saturation polarization of ceramics and reduced the residual polarization. Meanwhile, the introduction of LMZ significantly affects the microstructure and relaxor behavior of BNST-based ceramics, resulting in reduced grain size and a more compact ceramic structure. It was found that 0.85BNST-0.15LMZ ceramic exhibited decent energy storage performance under an electric field of 400&#xa0;kV/cm, with a large <i>W</i><sub>rec</sub> of 4.53&#xa0;J/cm and high <i>η</i> of 87.50%. It is noted that 0.85BNST-0.15LMZ ceramics exhibited ultra-fast discharge rate of 23&#xa0;ns. These results indicate that 0.85BNST-0.15LMZ ceramics have broad development prospects in the field of supercapacitors for energy storage.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Enhancement of energy storage performance of (Bi0.5Na0.5)0.7Sr0.3TiO3 ceramics by introducing La(Mg0.5Zr0.5)O3

  • 期刊论文

  • 发表日期：

    2025年5月25日

查看全文
  • Liangdong Li,
  • Haixiang Guo,
  • Ruiping La,
  • Shiling Huang,
  • Huanfu Zhou

摘要

With the development of pulsed power devices in the direction of miniaturization, integration, and safety, the development of dielectric capacitors with large energy storage density (Wrec), high energy storage efficiency (η), and decent energy storage stability has become an important topic that needs to be discussed in depth in the academic community. In this study, (1 − x)(Bi0.5Na0.5)0.7Sr0.3TiO3-xLa(Mg0.5Zr0.5)O3 [(1 − x)BNST-xLMZ] ceramics were prepared by traditional solid-phase method. Through rational component manipulation, the introduction of LMZ effectively disrupted the long-range ordered arrangement of the original matrix, constructing short-range polar nano-microregions that consequently delayed the saturation polarization of ceramics and reduced the residual polarization. Meanwhile, the introduction of LMZ significantly affects the microstructure and relaxor behavior of BNST-based ceramics, resulting in reduced grain size and a more compact ceramic structure. It was found that 0.85BNST-0.15LMZ ceramic exhibited decent energy storage performance under an electric field of 400 kV/cm, with a large Wrec of 4.53 J/cm and high η of 87.50%. It is noted that 0.85BNST-0.15LMZ ceramics exhibited ultra-fast discharge rate of 23 ns. These results indicate that 0.85BNST-0.15LMZ ceramics have broad development prospects in the field of supercapacitors for energy storage.