In the present work, we report the synthesis and investigations of La0.9K0.1MnO3 and La0.8K0.1Pb0.1MnO3 bulk samples which could be potential magnetocaloric materials for magnetic refrigeration close to room temperature. A flash combustion reaction and sintering at 1200 °C for 10 h are used to prepare the bulk materials. Both compounds crystallized into a rhombohedral structure with R \(\overline{3 }\) c space group confirmed by X-ray powder diffraction results. Scanning electron microscopy analysis, combined with XRD peak profiles is performed to estimate the particle/crystallite size of the samples. Moreover, the Curie temperature, TC, is found to be higher in lead-rich sample due to the enhancement of the grain size and the Mn3+–O–Mn4+ double exchange (DE) interaction. Therefore, the bulk sample La0.8K0.1Pb0.1MnO3 shows a room temperature phase transition of 289 K as well as a higher saturation magnetization. The La0.8K0.1Pb0.1MnO3 bulk compound exhibits a high and sharp peak in magnetic entropy change up to 5.5 Jkg−1 K−1 under 5 T at the magnetic transition temperature TC. To compare the magnetocaloric performances of the studied compounds, relative cooling power (RCP) was employed. The obtained experimental results revealed that the increase in particle size influences severely the magnetocaloric properties.