Ceramic Body Based on Kaolin – Alumina-Containing Waste – Dolomite System

The article investigates the high-temperature interaction and sintering processes of samples of low-temperature firing high-alumina for technical ceramics based on the kaolin – alumina-containing component – dolomite ternary system and establishes the areas of formation of high-alumina body for technical ceramics on the ternary diagram. It is shown that as a result of high-temperature interaction, the formation of new crystalline phases of minerals occurs, including mullite, corundum, β-cristobalite, as well as in a small amount of anorthite and an amorphous glassy phase, which impart the necessary physical and mechanical properties to the fired sample. The area of optimal compositions for obtaining low-temperature sintering high-alumina ceramic bodies based on the kaolin – alumina-containing waste – dolomite ternary system was determined.