Ceramic Dielectrics in the Oxide System ZrO2–SnO2–TiO2 for Microwave Technology
摘要
In this work, a study was made of the possibility of obtaining ceramics for microwave technology in the system of ZrO2–SnO2–TiO2 oxides by solid-phase synthesis using a sintering additive, lanthanum (III) oxide. Ceramics based on zirconium-tin titanate composition Zr0.8 Sn0.2 TiO4 with additions of 2, 4, and 6 wt.% La2O3, its properties were studied using various methods of analysis. The densest ceramic specimens were obtained at a firing temperature of 1400°C and a La2O3 content of 4 wt.%.