Eutectic Additive Influence in the Li₂O–B₂O₃ System on the Sintering Process and Properties of Li₂MgTi₃O₈ Ceramics

The effect of the eutectic additive of the system Li₂O–B₂O₃ on the sintering process and the dielectric properties of Li₂MgTi₃O₈-based ceramics was studied. It was found that the introduction of an additive in amounts 10.0 – 15.0% promotes sintering of ceramics by means of a liquid-phase mechanism. Li₂MgTi₃O₈-based ceramic, containing a sintering additive in the amount 15.0% and fired at 900°C, demonstrates the following property levels: average density ρ_av = 3.04 g/cm³, open porosity P_o = 5.7%, relative dielectric constant ε_r = 19.0, and dielectric loss tangent tan δ = 0.028. The lowered sintering temperature of the ceramic will allow the manufacture of different electronic components based on it, using low-temperature co-firing ceramic (LTCC) technology, and the a specified level of dielectric properties will allow the miniaturization of devices.