<p>To address the problem of dye wastewater pollution, hierarchical porous alumina ceramics (HPAC) were prepared as carriers in this study by using digital light processing (DLP) 3D printing combined with the freeze-drying method. The results showed that the hierarchical porous alumina ceramics with a porogenic agent content of 33 wt% exhibited the highest porosity of 34.20% ± 1.22% and a pore size of 2–5&#xa0;nm. An efficient photocatalytic system was constructed by loading nickel oxide nanoparticles (n-NiO) via the sol-gel method. The prepared photocatalytic carriers and photocatalysts were characterized for structural and morphological analysis using X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET) surface area analyzer, and energy-dispersive X-ray fluorescence spectroscopy (EDS). The results indicated that n-NiO/HPAC with 15.43% NiO loading achieved optimal performance in methylene blue (MB) degradation experiments, with the MB degradation rate reaching 94.51%. This study provides a theoretical basis and technical support for the practical application of porous-material-loaded n-NiO photocatalysts in dye wastewater treatment.</p> Graphical abstract <p></p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Preparation of Nickel Oxide-Loaded Hierarchical Porous Alumina Ceramic for Photocatalytic Degradation of Methylene Blue

  • 期刊论文

  • 发表日期：

    2025年4月16日

查看全文
  • Tao Liu,
  • Guangming Zhou,
  • Bingyan Yu,
  • Lihu Fu,
  • Simiao Yu,
  • Zhenjie Xu,
  • Gang Lu

摘要

To address the problem of dye wastewater pollution, hierarchical porous alumina ceramics (HPAC) were prepared as carriers in this study by using digital light processing (DLP) 3D printing combined with the freeze-drying method. The results showed that the hierarchical porous alumina ceramics with a porogenic agent content of 33 wt% exhibited the highest porosity of 34.20% ± 1.22% and a pore size of 2–5 nm. An efficient photocatalytic system was constructed by loading nickel oxide nanoparticles (n-NiO) via the sol-gel method. The prepared photocatalytic carriers and photocatalysts were characterized for structural and morphological analysis using X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET) surface area analyzer, and energy-dispersive X-ray fluorescence spectroscopy (EDS). The results indicated that n-NiO/HPAC with 15.43% NiO loading achieved optimal performance in methylene blue (MB) degradation experiments, with the MB degradation rate reaching 94.51%. This study provides a theoretical basis and technical support for the practical application of porous-material-loaded n-NiO photocatalysts in dye wastewater treatment.

Graphical abstract