<p>Organic-pillared vermiculite was applied as the support to fabricate Ru catalyst via adsorption-precipitation method. The catalytic performances of the catalyst were investigated for the selective hydrogenation of levulinic acid (LA) or methyl levulinate (ML) to γ-valerolactone (GVL). The 100% selectivity of GVL and 100% conversion of LA were obtained at 403&#xa0;K, 4.0&#xa0;MPa using water as solvent. Moreover, a good recyclability was observed even after 14 reaction cycles as a slight conversion decrease of the LA and no change of the selectivity of GVL. The Characterization of the fresh catalysts and reused catalysts were performed using various techniques including XRD, FT-IR, N<sub>2</sub> adsorption-desorption, XPS and TEM. The catalytic tests and characterization data confirmed that the sample of Ru/Modified-Vermiculite can be taken as a robust and effective catalyst for the conversion of the LA to GVL.</p> Graphical Abstracts <p></p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Modified Vermiculite Supported Ru Nanoparticles as a Robust Catalyst for the Hydrogenation of Levulinic Acid to γ-Valerolactone

  • 期刊论文

  • 发表日期：

    2025年1月28日

查看全文
  • Danhong Yang,
  • Shihong Chen,
  • Lei Wang,
  • Mingdeng Liu,
  • Lanping Lai,
  • Lina Zhou

摘要

Organic-pillared vermiculite was applied as the support to fabricate Ru catalyst via adsorption-precipitation method. The catalytic performances of the catalyst were investigated for the selective hydrogenation of levulinic acid (LA) or methyl levulinate (ML) to γ-valerolactone (GVL). The 100% selectivity of GVL and 100% conversion of LA were obtained at 403 K, 4.0 MPa using water as solvent. Moreover, a good recyclability was observed even after 14 reaction cycles as a slight conversion decrease of the LA and no change of the selectivity of GVL. The Characterization of the fresh catalysts and reused catalysts were performed using various techniques including XRD, FT-IR, N2 adsorption-desorption, XPS and TEM. The catalytic tests and characterization data confirmed that the sample of Ru/Modified-Vermiculite can be taken as a robust and effective catalyst for the conversion of the LA to GVL.

Graphical Abstracts