Does the universal adhesive’s film thickness affect dentin-bonding effectiveness?

To investigate the influence of adhesive resin application modalities on the film thickness of the adhesive resin and the effectiveness of a two-step universal adhesive (UA) bonded in self-etch (SE) bonding mode to high C-factor class-I cavity-bottom dentin.

After application of the primer of G2-Bond Universal (G2B, GC), the adhesive resin was applied into standard class-I cavities (human molars) following four application modalities: (1) one layer, strongly air-blown; (2) one layer, gently air-blown; (3) two layers, each gently air-blown; (4) one layer, not air-blown. After being restored with composite, each tooth was sectioned to obtain one micro-specimen (n = 10), of which the adhesive resin film thickness was measured using optical microscopy. The micro-tensile bond strength (μTBS) was tested immediately or upon 100,000 thermocycles. Statistical analyses involved Kruskal–Wallis and Mann–Whitney U testing (p < 0.05).

G2B’s μTBS was significantly affected by the adhesive resin application modality and aging. Gently air-blowing the adhesive resin resulted in significantly higher immediate μTBS than strong air-blowing or no air-blowing. No significant difference in μTBS was found between single or double gently air-blown adhesive resin applications. The adhesive resin film thickness significantly varied with the application modalities.

A too thin or too thick adhesive resin film thickness adversely affected bond strength of the two-step UA applied in SE mode and high C-factor condition.

The adhesive resin layer thickness can affect the bonding performance of two-step UAs in high C-factor cavities. Dental clinicians remain advised to avoid improper air-blowing of UAs and strictly follow the application instructions.