<p>In this work, the solid-state reaction strategy be present used headed for synthesize nanoparticle samples of Ce<sub>(2-(x+y+z)</sub> Gd<sub>x</sub>Cu<sub>y</sub>Dy<sub>z</sub>O<sub>2</sub>, at various concentrations of x, y, and z = 0.01, 0.03, 0.05. XRD analysis verified with cubic structure of both undoped and doped samples. Crystallite sizes ranged from 19.01 to 35.56&#xa0;nm, while lattice parameters increased from 5.478 to 5.832&#xa0;Å. The surface morphology (SEM) was primarily spherical and agglomerated at 500&#xa0;nm. The elemental analysis (EDS) revealed the predicted stoichiometric atomic ratio (Dy-Cu-Gd). According to the results of optical studies, the optical band gap of the powders increases from 2.749 to 3.185&#xa0;eV as the concentration increases. Photoluminescence investigations reveal blue, green, yellow, and ultraviolet emissions at different intensities in the emission spectrum. The magnetic parameters of the nanoparticle samples revealed paramagnetic features, the magnetic moment of Ce<sub>(2-(x+y+z)</sub> Gd<sub>x</sub>Cu<sub>y</sub>Dy<sub>z</sub>O<sub>2</sub> nanoparticles ranged from 0.0047 to 0.0785&#xa0;emu/g.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Dy-Cu-Gd triple doped CeO2 diluted magnetic semiconductor nanopowders: structural, optical, and magnetic properties

  • 期刊论文

  • 发表日期：

    2025年4月13日

查看全文
  • G. Chinna Venkata Subbaiah,
  • N. Madhusudhana Rao,
  • Nakka Praveenkumar

摘要

In this work, the solid-state reaction strategy be present used headed for synthesize nanoparticle samples of Ce(2-(x+y+z) GdxCuyDyzO2, at various concentrations of x, y, and z = 0.01, 0.03, 0.05. XRD analysis verified with cubic structure of both undoped and doped samples. Crystallite sizes ranged from 19.01 to 35.56 nm, while lattice parameters increased from 5.478 to 5.832 Å. The surface morphology (SEM) was primarily spherical and agglomerated at 500 nm. The elemental analysis (EDS) revealed the predicted stoichiometric atomic ratio (Dy-Cu-Gd). According to the results of optical studies, the optical band gap of the powders increases from 2.749 to 3.185 eV as the concentration increases. Photoluminescence investigations reveal blue, green, yellow, and ultraviolet emissions at different intensities in the emission spectrum. The magnetic parameters of the nanoparticle samples revealed paramagnetic features, the magnetic moment of Ce(2-(x+y+z) GdxCuyDyzO2 nanoparticles ranged from 0.0047 to 0.0785 emu/g.