<p>A comprehensive exploration of penta glass systems’ spectroscopic and dielectric characteristics was achieved, specifically for the glass series 20Li<sub>2</sub>O–15Fe<sub>2</sub>O<sub>3</sub>–5In<sub>2</sub>O<sub>3</sub>–xBi<sub>2</sub>O<sub>3</sub>–(60–x) P<sub>2</sub>O<sub>5</sub>(x = 0, 2.5, 5, 7.5, 10, and 12.5&#xa0;mol %). Both average phosphorus-phosphorus separation and crystalline volume were found to decrease depending on Bi<sub>2</sub>O<sub>3</sub> content. The optical band gap obtained from diffuse reflectance spectra (DRS) is found to be in the range of 1.58–1.81 eV with increasing bismuth oxide content. The optical band gap increases with bismuth content, which can be ascribed to structural changes and the reduction in non-bridging oxygen (NBO). A decrease in optical parameters, viz., refractive index (2.945–2.824), molar refractivity (32.45–29.12), and molar polarizability values (12.88–11.56), occurs with Bi<sub>2</sub>O<sub>3</sub> content. The glasses have been designated as semiconductors due to an increase in the metallization criteria values (M lie between 0.2811 and 0.3008). The obtained results exhibit contraction in the bonds of the glass matrix and an increase in rigidity of the structure at a higher content of Bi<sub>2</sub>O<sub>3</sub>.The dc and ac conductivity of the studied glasses were affected by the O/P ratio, as they attained high values at O/<i>P&#xa0;</i>&gt;&#xa0;3.0. The asymmetrical shape of the Nyquist semicircle indicated that the glasses behavior deviated from Debye relaxation. The overall behavior of the electrical properties of the studied glasses revealed their semiconducting performance. The examined glasses could be good choices for photonic applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Dielectric and spectroscopic features of Li2O/Fe2O3/In2O3/P2O5 glass systems doped with Bi2O3

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年1月8日

查看全文
  • Ebrahim A. Mahdy,
  • S. Ibrahim,
  • H. A. Abo-Mosallam,
  • Ahlam M. Fathi

摘要

A comprehensive exploration of penta glass systems’ spectroscopic and dielectric characteristics was achieved, specifically for the glass series 20Li2O–15Fe2O3–5In2O3–xBi2O3–(60–x) P2O5(x = 0, 2.5, 5, 7.5, 10, and 12.5 mol %). Both average phosphorus-phosphorus separation and crystalline volume were found to decrease depending on Bi2O3 content. The optical band gap obtained from diffuse reflectance spectra (DRS) is found to be in the range of 1.58–1.81 eV with increasing bismuth oxide content. The optical band gap increases with bismuth content, which can be ascribed to structural changes and the reduction in non-bridging oxygen (NBO). A decrease in optical parameters, viz., refractive index (2.945–2.824), molar refractivity (32.45–29.12), and molar polarizability values (12.88–11.56), occurs with Bi2O3 content. The glasses have been designated as semiconductors due to an increase in the metallization criteria values (M lie between 0.2811 and 0.3008). The obtained results exhibit contraction in the bonds of the glass matrix and an increase in rigidity of the structure at a higher content of Bi2O3.The dc and ac conductivity of the studied glasses were affected by the O/P ratio, as they attained high values at O/P > 3.0. The asymmetrical shape of the Nyquist semicircle indicated that the glasses behavior deviated from Debye relaxation. The overall behavior of the electrical properties of the studied glasses revealed their semiconducting performance. The examined glasses could be good choices for photonic applications.