Investigating the impact of local Libyan grasses: Stipa tenacissima and Retama raetam on mechanical properties of styrene-butadiene rubber composites

This paper presents a comparative study on the effect of two local Libyan grasses, Stipa tenacissima (locally known as Halfa) and Retama raetam (locally known as R’tem) on the mechanical properties of styrene-butadiene rubber composites (SBR). For this purpose, the effect of filler type and content (10, 20, 30 and 40 wt%) on the mechanical properties of the composites including stress at break, elongation at break, impact strength and microhardness were evaluated. The stress at break of SBR increased only with the addition of 20 wt% and 30 wt% of Halfa. The highest value of stress at break was obtained by composites made with 20 wt% Halfa content. The elongation at break was significantly decreased with the addition of Halfa and R’tem. Generally, the elongation at break of the composites made with R’tem was slightly higher than that of composites made with Halfa. On the other hand, the addition of Halfa resulted in composites with relatively higher impact properties. The impact strength of these composites was increased with increasing the Halfa content up to 30 wt% after which it was decreased noticeably. However, the impact strength of composites made with R’tem did not follow a clear path with increasing R’tem content. Furthermore, the incorporation of Halfa and R’tem resulted in a significant increase in the hardness properties of the composites. R’tem showed to produce composites with higher hardness compared to those made with Halfa. Composites made with Halfa possess better toughness and ductility to a certain degree in comparison to composites made with R’tem. Although, Halfa appears to be relatively better than R’tem in reinforcing SBR, both fillers appeared to be good candidate filler to produce low cost and density polymer composites with acceptable mechanical properties.