<p>This study investigates the friction stir welding (FSW) of a CuNiSiCr alloy produced by laser powder bed fusion and the role of post-weld heat treatments in the microstructural evolution and mechanical performance of welded joints. The as-built alloy exhibited columnar grains, porosity, and lack-of-fusion defects. FSW refined the microstructure within the stir zone (SZ) and dramatically reduced porosity, both in pore number and size, as revealed by X-ray tomography. Mechanical testing showed that FSW joints outperformed the as-built specimens, with increased yield and tensile strengths, albeit with reduced ductility. Aging at 500&#xa0;°C markedly enhanced hardness across both the base material and the SZ, achieving peak values of about 195 HV after 2&#xa0;h. Peak-aged joints reached yield and tensile strengths that were&#xa0;17% and 16% higher, respectively, than those of the base alloy. Direct aging proved as effective as conventional solution treatment and aging, simplifying the heat treatment route. These findings show that FSW followed by direct aging offers a promising approach for obtaining high-performance joints, providing a viable pathway for producing large, complex, additively manufactured CuNiSiCr assemblies with improved structural integrity.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Friction stir welding of additively manufactured CuNiSiCr: effect of post-weld heat treatments on microstructure and mechanical properties

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年11月20日

查看全文
  • Mohammad Abankar,
  • Vincenzo Lunetto,
  • Pasquale Russo Spena

摘要

This study investigates the friction stir welding (FSW) of a CuNiSiCr alloy produced by laser powder bed fusion and the role of post-weld heat treatments in the microstructural evolution and mechanical performance of welded joints. The as-built alloy exhibited columnar grains, porosity, and lack-of-fusion defects. FSW refined the microstructure within the stir zone (SZ) and dramatically reduced porosity, both in pore number and size, as revealed by X-ray tomography. Mechanical testing showed that FSW joints outperformed the as-built specimens, with increased yield and tensile strengths, albeit with reduced ductility. Aging at 500 °C markedly enhanced hardness across both the base material and the SZ, achieving peak values of about 195 HV after 2 h. Peak-aged joints reached yield and tensile strengths that were 17% and 16% higher, respectively, than those of the base alloy. Direct aging proved as effective as conventional solution treatment and aging, simplifying the heat treatment route. These findings show that FSW followed by direct aging offers a promising approach for obtaining high-performance joints, providing a viable pathway for producing large, complex, additively manufactured CuNiSiCr assemblies with improved structural integrity.