<p>This study examines the fabrication of toothed wheels from 316L stainless steel using powder bed fusion (PBF), evaluating surface roughness, dimensional fidelity, and mechanical performance in the as-built condition. Results reveal near-net shape (NNS) accuracy, within ± 0.05&#xa0;mm of the intended geometry, and a tensile strength of 720&#xa0;MPa, exceeding many traditional manufacturing processes. The rapid cooling characteristic of PBF induces a refined, nearly pore-free microstructure, driving Vickers hardness values up to 244.5 HV. Although no post-processing was used, average surface roughness remained at a modest 27.5&#xa0;µm (ISO 1302 N11), emphasizing PBF’s ability to fabricate complex features without compromising the overall finish. Thermodynamic simulations illustrate that secondary carbide formation and internal stresses contribute to the alloy’s improved strength, though the emergence of the sigma phase could locally reduce corrosion resistance. These findings emphasize the potential of PBF to deliver both dimensional precision and mechanical robustness in components subject to high-load, high-precision applications. Looking ahead, expanding the range of materials and refining process parameters, including laser power and scanning speed, offer promising directions for further performance gains and broader industrial adoption.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Surface analysis and mechanical properties of stainless steel 316L toothed wheel manufactured by powder bed fusion

  • 期刊论文

  • 发表日期：

    2025年3月11日

查看全文
  • Omid Ashkani,
  • Mohammad Rezayat,
  • Sina Fathi,
  • Abdellatif M. Sadeq,
  • Hamid Mehrabi,
  • Mark Armstrong

摘要

This study examines the fabrication of toothed wheels from 316L stainless steel using powder bed fusion (PBF), evaluating surface roughness, dimensional fidelity, and mechanical performance in the as-built condition. Results reveal near-net shape (NNS) accuracy, within ± 0.05 mm of the intended geometry, and a tensile strength of 720 MPa, exceeding many traditional manufacturing processes. The rapid cooling characteristic of PBF induces a refined, nearly pore-free microstructure, driving Vickers hardness values up to 244.5 HV. Although no post-processing was used, average surface roughness remained at a modest 27.5 µm (ISO 1302 N11), emphasizing PBF’s ability to fabricate complex features without compromising the overall finish. Thermodynamic simulations illustrate that secondary carbide formation and internal stresses contribute to the alloy’s improved strength, though the emergence of the sigma phase could locally reduce corrosion resistance. These findings emphasize the potential of PBF to deliver both dimensional precision and mechanical robustness in components subject to high-load, high-precision applications. Looking ahead, expanding the range of materials and refining process parameters, including laser power and scanning speed, offer promising directions for further performance gains and broader industrial adoption.