<p>In this study, a brand new bamboo scrimber–rubberwood CLT (BRCLT) has been proposed, along with one-component polyurethane (PUR) adhesive. Three processing factors were considered, pressure (1.5&#xa0;MPa and 2.0&#xa0;MPa), glue spread rate (150&#xa0;g m<sup>−2</sup> and 200&#xa0;g m<sup>−2</sup>), and application of a water-based surface modifier. The bonding performance of BRCLT was examined by conducting block shear, delamination, short-span flatwise shear and four-point bending tests. It was found that (1) the optimal gluing process for fabricating BRCLT was a pressure of 2&#xa0;MPa, a glue spread rate of 150&#xa0;g/m<sup>−2</sup>, and the application of a water-based surface modifier. (2) The modifier significantly reduced the delamination rate of BRCLT. (3) BRCLT produced using the optimal bonding parameters can meet V1-grade CLT in terms of maximum shear stress, modulus of rupture (MOR), and modulus of elasticity (MOE), as stipulated in the American standard ANSI/APA PRG 320, suggesting BRCLT had a great potential to be a new member of CLT family.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

An investigation of the bond quality in the production of bamboo scrimber-rubberwood cross laminated timber

  • 期刊论文

  • 发表日期：

    2025年6月10日

查看全文
  • Benhao Miao,
  • Xiaojuan Jia,
  • Yan Xiao,
  • Meng Gong,
  • Peixing Wei,
  • Brad Jianhe Wang,
  • Suyong Huang

摘要

In this study, a brand new bamboo scrimber–rubberwood CLT (BRCLT) has been proposed, along with one-component polyurethane (PUR) adhesive. Three processing factors were considered, pressure (1.5 MPa and 2.0 MPa), glue spread rate (150 g m−2 and 200 g m−2), and application of a water-based surface modifier. The bonding performance of BRCLT was examined by conducting block shear, delamination, short-span flatwise shear and four-point bending tests. It was found that (1) the optimal gluing process for fabricating BRCLT was a pressure of 2 MPa, a glue spread rate of 150 g/m−2, and the application of a water-based surface modifier. (2) The modifier significantly reduced the delamination rate of BRCLT. (3) BRCLT produced using the optimal bonding parameters can meet V1-grade CLT in terms of maximum shear stress, modulus of rupture (MOR), and modulus of elasticity (MOE), as stipulated in the American standard ANSI/APA PRG 320, suggesting BRCLT had a great potential to be a new member of CLT family.